Posted: 04 July 2005 at 1:14am | IP Logged Quote excel
What is the Effect of phosphorus content on the salt spray corrosion resistance In electroless nickel ?

__________________
Excel
Back to Top View excel's Profile Search for other posts by excel
 
connect2raj
Newbie
Newbie
Avatar

Joined: 16 February 2007
Location: United States
Online Status: Offline
Posts: 1
Posted: 16 February 2007 at 6:01pm | IP Logged Quote connect2raj

In general, higher phosphorous alloy deposits tend to be more corrosion resistant especially in acid environments. A higher phosphorous alloy deposit will most certainly have better salt spray corrosion resistance then low phosphorous alloys.

 

 

 
Back to Top View connect2raj's Profile Search for other posts by connect2raj
 

If you wish to post a reply to this topic you must first login
If you are not already registered you must first register

  Post ReplyPost New Topic
Printable version Printable version

Forum Jump
You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot delete your posts in this forum
You cannot edit your posts in this forum
You cannot create polls in this forum
You can vote in polls in this forum



This page was generated in 0.1250 seconds.